Study of the interaction of components in the Sm-Pd-Ge systemстатья
Информация о цитировании статьи получена из
Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 29 мая 2015 г.
Аннотация:Interaction of components in the Sm-Pd-Ge system was investigated by methods of physicochemical analysis. Isothermal section of the phase diagram at 870 K was constructed and new ternary intermetallic compounds formed in the system were studied. Formation often new ternary intermetallic compounds Sm3Pd20-18.5Ge6-7.5, SmPd2.50-1.75, Ge-1.50-2.25, Sm2Pd3Ge5, Sm2PdGe5, SmPd3Ge, SmPd0.8-0.5, Ge-1.2-1.5, SmPd3Ge, SmPd2Ge, SmPdGe2, SmPdGe, SmPd0.8-0.5, Ge-1.2-1.5, and Sm2PdGe was established. The crystal structure of all ternary intermetallic compounds (two of them were known before) was determined and adjusted