Effect of preparation conditions on gas permeability and sealing efficiency of graphite foil

Vladimirovich, I.A.; Manylov, M.S.; Maksimova, N.V.; Kirichenko, A.N.; Filimonov, S.V.; Malakho, A.P.; Avdeev, V.V.

Авторы: Ivanov Andrei Vladimirovich, Manylov Mikhail S., Maksimova Natalia V., Kirichenko Alexey N., Filimonov Stanislav V., Malakho Artem P., Avdeev Victor V.
Журнал: Journal of Materials Science
Том: 54
Номер: 5
Год издания: 2019
Издательство: Springer Nature
Местоположение издательства: Switzerland
Первая страница: 4457
Последняя страница: 4469
DOI: 10.1007/s10853-018-3151-1
Аннотация: Nitrogen permeability of graphite foil (GF) based on expandable graphite with different oxidation degrees was measured. Expandable graphite was obtained by the chemical interaction of graphite and nitric acid with the formation of graphite nitrate of II, III, IV stages and by the electrochemical oxidation of graphite in HNO3 solution followed by water washing. The expandable graphite samples were heat-treated at 800 deg.C with the formation of exfoliated graphite followed by pressing the exfoliated graphite into GF. The samples of exfoliated graphite and graphite foil were investigated by XRD, SEM, Raman spectroscopy and mercury porosimetry methods. GF nitrogen permeance decreases from 19.7x10^-10 to 6.7x10^-10 mol*m^-2*s^-1*Pa^-1 with decreasing a stage number of graphite nitrate from IV to II. Gas permeance of GF based on electrochemical expandable graphite decreases by an order of magnitude up to 0.2x10^-10 mol*m^-2*s^-1*Pa^-1 in comparison with GF based on graphite nitrate of II stage. Thus, it is possible to produce the graphite foil material with a wide range of permeability and, respectively, the different sealing efficiency by varying the oxidation degree of the initial graphite matrix in the step of obtaining graphite intercalation compounds and expandable graphite.
Добавил в систему: Манылов Михаил Сергеевич

	ИСТИНА	Войти в систему Регистрация
	ИПМех РАН
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

ИПМех РАН

Effect of preparation conditions on gas permeability and sealing efficiency of graphite foilстатья Исследовательская статья

Прикрепленные файлы