Аннотация:R:YAB thin films were grown from K2Mo3O10-B2O3 based fluxed melts using substrates made of nominal pure YAl3(BO3)4 crystals. Growth kinetics, micromorphology and composition of Yb:YAB and NAB thin films were studied in dependence on supersaturation and temperature regime of fluxed melts.