Synthesis, structure, and conductivity of alluaudite-related phases in the Na2MoO4–Cs2MoO4–CoMoO4 systemстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 11 апреля 2019 г.
- Авторы: Yudin Vasiliy N., Zolotova Evgeniya S., Solodovnikov Sergey F., Solodovnikova Zoya A., Korolkov Iliya V., Stefanovich Sergey Yu, Kuchumov Boris M.
- Журнал: European Journal of Inorganic Chemistry
- Том: 2019
- Номер: 2
- Год издания: 2019
- Издательство: John Wiley & Sons Ltd.
- Местоположение издательства: United Kingdom
- Первая страница: 277
- Последняя страница: 286
- DOI: 10.1002/ejic.201801307
- Аннотация: Phase formation study of the Na2MoO4–Cs2MoO4–CoMoO4 system resulted in new cesium‐containing alluaudite‐related phases. The solid solution Na4–2x‐yCsyCo1+x(MoO4)3(0 ≤ x, y ≤ 0.30), based on the alluaudite‐type Na4–2xCo1+x(MoO4)3, and triple molybdate Na10(Cs4‐xNax)Co5(MoO4)12 (0 ≤ x ≤ 0.30) were found, and their structures were solved. In the structure of Na3.21Cs0.37Co1.21(MoO4)3 (a = 13.0917(8) Å, b = 13.5443(8) Å, c = 7.1217(4) Å, space group C2/c, β = 112.331(2), Z = 4), the cesium ions partially substitute the Na+ in the channels running along the c‐axis. The structure of Na10(Cs3.77Na0.23)Co5(MoO4)12 (a = 13.6572(3) Å, b = 11.5063(3) Å, c = 27.9898(5) Å, space group Pbca, Z = 4) was proved to be the aristotype for the pseudo orthorhombic Na25Cs8R5(MoO4)24 (R = Fe, Sc, In). The compounds contain alluaudite‐like layers of MoO4 tetrahedra and pairs of edge‐shared (Co, Na)O6 or (R, Na)O6 and NaO6 octahedra, which are connected by bridging MoO4tetrahedra to form 3D frameworks differing from the alluaudite type. The frameworks contain channels along the c‐axis filled by Cs+ and Na+ ions. Bond valence sum (BVS) maps show that the alluaudite‐related molybdates can have a 2D sodium‐ion conductivity at elevated temperatures in contrast to the alluaudite‐type cathode material Na2+2xFe2‐x(SO4)3 with a 1D conductivity. The measured ionic conductivity of Na4–2xCo1+x(MoO4)3, Na4–2x‐yCsyCo1+x(MoO4)3, and Na10Cs4Co5(MoO4)12 reaches 10–3 – 10–2 S cm–1 at 500 °C.