Fracture properties of graphite materials and analysis of crack growth under bending conditionsстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 11 сентября 2018 г.

Работа с статьей


[1] Lomakin E. V., Tretyakov M. P. Fracture properties of graphite materials and analysis of crack growth under bending conditions // Meccanica. — 2016. — Vol. 51, no. 10. — P. 2353–2364. The elastic and strength properties of different grades of graphite materials as well as their fracture toughness properties are studied. The method for the determination of crack length and the values of fracture toughness characteristics of materials during stable equilibrium crack growth under bending conditions is considered. The unstable or non-equilibrium crack growth from short initial crack is observed in experiments, and corresponding theoretical explanation is given. The process of unstable crack growth is analyzed for different loading conditions. It has been shown that in the cases of short cracks, some part of stored energy transforms into kinetic energy, which can be described by the equation of energy balance during unstable crack growth. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть