Аннотация:The three generically accepted stages of glass corrosion are reviewed with
focus on final stage termed alteration rate renewal (or resumption) stage when the glass may
re-start corroding with the rate similar to that at the initial stage. It is emphasized that
physical state and physical changes that occur in the near-surface layers can readily lead to
an effective increase of leaching rate which is similar to alteration rate renewals.
Experimental data on long-term (during few decades) corrosion of radioactive borosilicate
glass K26 designed to immobilize high-sodium operational NPP radioactive waste evidence
on resumption-like effects of radionuclides (137,134Cs) leaching. The cause of that was however
related not to chemical changes in the leaching environment but rather to physical state of
glass surface due to formation of small cracks and new pristine glass areas in contact with
water.