The cobalt and nickel-containing polyethylene prepared by using metal-vapor synthesisingстатья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 21 октября 2020 г.
Аннотация:Cobalt and nickel-containing low-pressure polyethylene samples (HDPE) wereprepared by metal-vapor synthesis (MVS) of unstable bisarene complexes of Ni and Co type(C6H5CH3)2M and their further decomposition at a temperature of 178 K in the volume ofHDPE. The Faraday method shows that Ni and Co nanometer particles are stabilized by thepolyethylene matrix up to T=370 K. When the Ni-HDPE material is heated above 420 K,irreversible processes of interaction of Ni clusters with the polyethylene matrix occur with theformation of a less magnetic phase. When the Co-HDPE material is heated above 420 K, Coclusters coalesce to form a more magnetic phase. At temperatures above 520 K, themagnetization of the Co/HDPE system begins to increase rapidly and approaches the valuecharacteristic of massive cobalt. Changing the conditions of cryosynthesis significantlyinfluences the properties of the resulting products. The sample of 2.5% Co-HDPE obtained at atemperature of 185 K is characterized by weak magnetic properties. Its magnetization at roomtemperature is lower than that of the samples with a similar metal content by 30-40 times. TheXPS shows that nickel atoms are in the form of Ni(OH)2.