Microstructure and phase composition of Al-Ce-Cu alloys in the Al-rich cornerстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 7 октября 2020 г.
Аннотация:Al-Cu-Ce alloys have been studied in the Al-rich corner using the microstructural (LM and SEM), thermal (direct and DSC), X-ray diffraction and electron probe microanalysis techniques. Three cross-sections were of particular interest: (a) at 20%Cu (up to 12.5%Ce), (b) at 14%Cu (up to 10%Cu) and (c) at a ratio Cu:Ce=2:1 (up to 10%Ce and 20%Cu). As-cast alloys and those after annealing at 540 and 590°C were studied. Boundaries of appearance of the Al8CeCu4 primary crystals and ternary eutectic involving the phase Al2Cu were determined. The radial cross section (Cu:Ce=2:1) is supposed to be of quasibinary type as ternary eutectic does not form. The temperature and concentrations of the eutectic reaction L-(Al)+CeCu 4Al8 were found to be 610°C, 14%Cu and 7%Ce. This binary eutectic has fine microstructure and is capable to fragmentation and spheroidization during heating. The paper considers possibility of using the Al-Cu-Ce system for developing novel Al casting alloys with significantly improved casting properties (hot tearing and fluidity) in comparison with 2xx commercial alloys.