Preparation of Magnetic Coatings from Strontium Hexaferrite on Tin and Cardboard by Cold Rollingстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:A timely dispersed powder of strontium hexaferrite doped with aluminium of the composition SrFe12-xAlxO19 with an aluminium content x = 0.6 +/- 0.1 is prepared through crystallization of oxide glasses. The powder is characterized by a saturation magnetization of 60.2 A m(2)/kg and it coercive force of 550 kA/m. The hexaferrite particles predominantly have the shape of thick hexagonal platelets with a diameter ranging front 300 to 500 nm and a thickness-to-diameter ratio varying from 0.3 to 0.5. Magnetic coatings on tin and cardboard substrates are produced by cold rolling of strontium hexaferrite powders. It is shown that hexaferrite particles in the magentic coatings have the preferred orientation of the well-developed facets along the rolling plane, which manifests itself in anisotropy of the magnetic properties of the coatings. The degree of texturing in the strontium hexaferrite coatings on cardboard and tin substrates is equal to 44 and 66%, respectively.