A study of the physical and mechanical properties of aerogels obtained from bacterial celluloseстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 6 октября 2021 г.
Аннотация:Aerogels with a density of 4.2-22.8 kg/m3 were obtained from bacterial cellulose synthesized in static and dynamic cultivation conditions on a molasses medium. The strength properties and porous structure of the aerogels strongly depended on their density. With a 22.8 kg/m3 aerogel density, the modulus of elasticity at 80% compression of the sample was 0.1 MPa. The decrease in the density of aerogels led to an increase in the pore sizes ranging from 20 µm to 1000 µm and a decrease in the modulus of elasticity. These characteristics were more pronounced in aerogels obtained from bacterial cellulose in static cultivation conditions. The aerogels had a low coefficient of thermal conductivity (0.0257 W/m*°С), which is comparable with the thermal conductivity of air, and moderate thermal stability since the degradation processes of the aerogels began at 237 °C. The aerogels obtained from bacterial cellulose had high sound absorption coefficients in the frequency range of 200-5000 Hz, which makes it possible to use as heat- and sound-insulating materials.