Interaction between La0.7Sr0.3MnO3 and SrZrO3 in CMR compositesстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Annealing of pressed mechanical mixtures of finely grained La0.7Sr0.3MnO3 and coarse-grained SrZrO3 at T=1000-1300degreesC was accompanied by a systematic decrease in SrZrO3 lattice parameters with increasing La0.7Sr0.3MnO3 : SrZrO3 ratio and a corresponding decrease in sample magnetization at room temperature. EDX nanoprobe analysis of the composites confirmed substantial out-diffusion of La and Mn from La0.7Sr0.3MnO3 into the SrZrO3 particles. This process, detectable at 1100degreesC, leads to an almost Uniform distribution of La and Mn (6-8%) in the SrZrO3 grains and the corresponding changes in manganite particle composition at 1300degreesC. Zr diffusion backflow is almost absent.