Growth of thin vanadia nanobelts with improved lithium storage capacity in hydrothermally aged vanadia gelsстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:A process of hydrothermal ageing of vanadia gels yields 10-20 nm thick and 90-100 nm wide nanobelts exceeding 10 microns in length. The diminished thickness and networking of anisotropic nanobelts lead to lithium intercalation capacities exceeding 450-500 mA h g(-1) at a C/25 rate. The observed morphology features depend essentially on preparation conditions and allow to assume that this particular route results in a suitable morphology of nanobelts via chemical bond rearrangement in the course of olation and oxolation in the aged bulk gel. "Unzipping'' of the layered structure of the precursor gel into single-crystalline nanobelts, and optimization of post-hydrothermal processing resulted in nanomaterials with enhanced electrochemical characteristics, making vanadia gels a precursor of choice for simple preparation of new battery nanomaterials.