Аннотация:The aim of the study was to develop a diagnostic method for the quantitative determination of the main components of cartilage tissueof various types based on multivariate IR spectral analysis and verification of data using classical chemical analysis.Materials and Methods. Cartilages of the nasal septum, knee joint, rib, and nucleus pulposus of the intervertebral disc, as well astrypsinized and defective cartilage samples, were examined as samples. The IR spectra of the cartilage samples, as well as calibrationmixtures of collagen and chondroitin sulfate, were obtained. The IR spectra were collected using the attenuated total reflectance techniques,and their processing was performed using the TQ Analyst software and the principal component regression calibration technique. Basedon calibration dependence, the Ksp coefficient was determined as the ratio of the mass fractions of collagen and chondroitin sulfate. Itsvalue was compared with the value of Kchem, equal to the ratio of the mass fractions of collagen and chondroitin sulfate, obtained using theclassical chemical analysis of these substances.Results. The IR spectra of cartilage tissues are a superposition of the IR spectra of collagen and chondroitin sulfate and qualitativelyreflect their composition. A change in the ratio between the relative intensities of the characteristic bands of compounds in the IR spectrumis obvious only with a significant change in the content of these compounds in cartilage. This change occurs after trypsinization, when Kspincreases from 0.88±0.05 (Kchem~0.8) to 4.55. The use of a calibration model with a complete analysis of the cartilage IR spectrum madeit possible to determine the difference in the ratio of the main components in the matrix of different samples in the absence of obviouschanges in the IR spectra. Thus, a statistically significant decrease in the content of chondroitin sulfate in degraded articular cartilage(Ksp=4.4±1.8; Kchem~5.5) was shown compared with intact samples (Ksp=2.8±1.1; Kchem~2.6).Conclusion. IR spectrometric express analysis of cartilage tissue employing the principal component regression method allows acorrect determination of the ratio of the main components in the cartilage matrix, those of collagen and glycosaminoglycans. The proposedtechnique includes one measurement, does not require prolonged and laborious sample preparation, does not require long, multi-stage andlaborious chemical manipulations to determine each of the components, and makes it possible to determine the features and changes in thecomposition for a large set of samples of cartilage tissue of different types. In future, this approach can be used for non-invasive diagnosticsof cartilage tissue.Key words: cartilage tissue; collagen; glycosaminoglycans; IR spectroscopy with attenuated total reflection; principal componentregression method.How to cite: Ignatieva N.Yu., Zakharkina O.L., Sviridov A.P. Express analysis of cartilage tissue using multivariate analysis of IRspectra. Sovremennye tehnologii v medicine 2022; 14(6): 25, https://doi.org/10.17691/stm2022.14.6.03