Thermal Stability of NASICON-Type Na3V2(PO4)3 and Na4VMn(PO4)3 as Cathode Materials for Sodium-ion Batteries

Авторы: Samigullin Ruslan R., Zakharkin Maxim V., Drozhzhin Oleg A., Antipov Evgeny V.
Журнал: Energies
Том: 16
Номер: 7
Год издания: 2023
Издательство: MDPI
Местоположение издательства: Basel, Switzerland
Первая страница: 3051
DOI: 10.3390/en16073051
Аннотация: The thermal stability of NASICON-type cathode materials for sodium-ion batteries was studied using differential scanning calorimetry (DSC) and in situ high-temperature powder X-ray diffraction (HTPXRD) applied to the electrodes in a pristine or charged state. Na3V2(PO4)3 and Na4VMn(PO4)3 were analyzed for their peak temperatures and the exothermic effect values of their decomposition processes, as well as the phase transformations that took place upon heating. The obtained results indicate that Mn-substituted cathode material demonstrates much poorer thermal stability in the charged state, although pristine samples of both materials exhibit similar thermal behavior without any DSC peaks or temperature-induced phase transitions in the studied temperature range. The in situ HTPXRD revealed the amorphization of desodiated Na4VMn(PO4)3-based electrodes occurring at 150~250 °C.
Добавил в систему: Самигуллин Руслан Ринатович

	ИСТИНА	Войти в систему Регистрация
	ИПМех РАН
	Главная Поиск Статистика О проекте Помощь

ИСТИНА