Wetting and spreading of molten NaCl and CaCl2 over polycrystalline hydroxyapatite

Gusev, S.A.; Shekhirev, M.A.; Safronova, T.V.; Putlayev, V.I.; Skvortsova, Z.N.; Protsenko, P.V.

Авторы: Gusev Sergey A., Shekhirev Mikhail A., Safronova Tatyana V., Putlayev Valerii I., Skvortsova Zoya N., Protsenko Pavel V.
Журнал: Mendeleev Communications
Том: 24
Год издания: 2014
Издательство: Elsevier BV
Местоположение издательства: Netherlands
Первая страница: 12
Последняя страница: 14
DOI: 10.1016/j.mencom.2013.12.003
Аннотация: The contact angles of molten NaCl and CaCl2 on hydroxyapatite (HAp) in air at 866 and 880 °C are close to zero. Wettability and the kinetics of spreading in the NaCl/HAp system were not affected by the reaction product presaturation of a melt or by substrate density and roughness; the rate of spreading for NaCl/HAp was described by the De Genes model of viscous dissipation, while it slowed down significantly in case of CaCl2 /HAp due to the interfacial reaction resulting in a surface tension gradient. Краевой угол смачивания расплавов NaCl и CaCl2 на поверхности гидроксиапатита на воздухе при 866 и 880 °C близки к 0. Смачиваемость и кинетика растекания в системе NaCl/гидроксиапатит не зависит от продуктов реакции в расплаве или плотности и характера поверхности субстрата; скорость растекания системе NaCl/гидроксиапатит описывается моделью вязкой диссипации De Genes, тогда как скорость растекания замедляется существенно в системе CaCl2/гидроксиапатит благодаря межфазной реакции, приводящей к возникновению градиента поверхностного натяжения. Ключевые слова: Краевой угол смачивания, гидроксиапатит, NaCl, CaCl2, растекание, межфазная реакция
Добавил в систему: Сафронова Татьяна Викторовна

	ИСТИНА	Войти в систему Регистрация
	ИПМех РАН
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

ИПМех РАН

Wetting and spreading of molten NaCl and CaCl2 over polycrystalline hydroxyapatiteстатья

Прикрепленные файлы