Effect of Hydrogenation on the Magnetic and Magnetocaloric Properties of Rare Earth Intermetallic Compounds Tb0.33Ho0.33Er0.33Ni and Dy0.33Ho0.33Er0.33Niстатья
- Авторы: Mohapatra Abhaya Prasada, Dhanya A.R., Chelvane J.Arout, Morozkin A.V., Ramaprabhu S., Nirmala R.
- Журнал: Journal of Superconductivity and Novel Magnetism
- Номер: 37
- Год издания: 2024
- Издательство: Springer Verlag
- Местоположение издательства: Germany
- Первая страница: 1223
- Последняя страница: 1228
- DOI: 10.1007/s10948-024-06747-0
- Аннотация: FeB-type structure (Space group Pnma, No. 62, oP8) and order ferromagnetically at 59 K and 40 K (TC) respectively. Hydrides of these samples show a presence of ~ 10-nm size nanoparticles with unit cell volume expansion. Magnetization measurements reveal that hydrides Tb0.33Ho0.33Er0.33NiH1.9 and Dy0.33Ho0.33Er0.33NiH1.9 remain paramagnetic from 300 K down to 5 K. Magnetization value at 5 K in 70 kOe field is ~ 5.1 μB/f.u. and 5.5 μB/f.u., respectively, for Tb0.33Ho0.33Er0.33NiH1.9 and Dy0.33Ho0.33Er0.33NiH1.9 samples. Despite the lack of ferromagnetic order, hydrides exhibit large low-temperature magnetocaloric effect with maximum isothermal magnetic entropy change values of about -11.6 J/kg*K at 14 K and -12.9 J/kg*K at 8 K respectively for 50 kOe magnetic field change.
- Добавил в систему: Морозкин Александр Владимирович
Прикрепленные файлы
| № | Имя | Описание | Имя файла | Размер | Добавлен |
|---|---|---|---|---|---|
| 1. | ЗАКЛЮЧЕНИЕ о возможности открытого опубликования 18.10.2024 № 112.2031.2024 | Заключение_112-2031-2024.pdf | 388,4 КБ | 3 апреля 2025 [morozkin] |