Modified Fe<sub>3</sub>O<sub>4</sub> Magnetite Core@Shell Type Nanomaterials for Highly-Responsive LPG Sensing: A Comparative Analysisстатья
- Авторы: Singh Shakti, Dzeranov Artur, Bondarenko Lyubov, Kydralieva Kamila, Dzhardimalieva Gulzhian, Babaytsev Arseniy, Kugabaeva Gulsara, Golubeva Nina, Yadav Bal Chandra
- Журнал: ECS Sensors Plus
- Том: 2
- Номер: 1
- Год издания: 2023
- Издательство: IOP Publishing Limited
- Местоположение издательства: United States
- Первая страница: 013601
- Последняя страница: 013601
- DOI: 10.1149/2754-2726/acc3ab
- Аннотация: The present work focuses on the synthesis of Fe3O4 magnetite core@shell type nanoparticles modified with three types of ligands: Magnetite with activated carbon (MAC), Magnetite with silica (tetraethoxysilane, TEOS, and 3-aminopropyltriethoxysilane, APTES) (MTA) and Magnetite with silica, APTES and humic acids (MTAH). The MTAH sample shows greater porosity in comparison to MTA, and MAC samples. The band gap of MTAH is 4.08 eV, which is higher than MTA (2.92 eV), and MAC (2.80 eV). Rietveld quantitative phase analysis of all derivatives was performed and compared with all three samples. The LPG sensing at room temperature shows the highest sensor response of 9.42, in comparison to 3.87 sensor response for MAC, and 4.60 for MTA. This approximately double sensor response increment is justified with the help of band gap, porosity, and size of all 3 the samples. The MTAH sample shows the lowest response-recovery time of 9.33 and 10.78 s respectively in comparison to MAC and MTA samples. In conclusion, this manuscript describes the synthesis procedure of different derivatives of Fe3O4 core@shell materials along with the relation of LPG sensing with different parameters of the materials.