Radiation-chemical synthesis of poly(vinyl alcohol) hydrogel containing dicyclohexano-18-crown-6статья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Radiation-chemical synthesis of poly(vinyl alcohol) hydrogels containing physically immobilized dicyclohexano-18-crown-6 was carried out. Remarkable gel fraction of 40-70% was observed at absorbed dose of about 5 kGy. Increasing degree of poly(vinyl alcohol) crosslinking led to growth of the efficiency of crown ether immobilization. Post-irradiation thermal annealing of the hydrogel samples at 120 degrees C for 0.5-5 h resulted in an increase of crown ether retention as compared with non-annealed samples by approximately 20% at the same absorbed dose. Preliminary results on a sorption behavior of the crown-containing hydrogels with respect to Sr2+ cations in 2.4 M HNO3 solution are presented. (c) 2007 Elsevier B.V. All rights reserved.