Sawdust as an effective biotemplate for the synthesis of Ce0.8Zr0.2O2 and CuO-Ce0.8Zr0.2O2 catalysts for total CO oxidationстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 19 декабря 2017 г.
Аннотация:Wood sawdust (SD) was successfully used as a biotemplate to prepare precursors of Ce0.8Zr0.2O2 (CZ) and CuO-Ce0.8Zr0.2O2 (Cu-CZ, about 25% of CuO) catalysts, which were tested in total CO oxidation at 100-400 [degree]C after calcination at 500 or 600 [degree]C, and compared with analogous systems prepared using cetyltrimethylammonium bromide (CTAB). The improved specific surface area and oxygen mobility of the catalysts calcined at 500 [degree]C resulted in an increased efficiency in CO oxidation. CZ (SD-500) demonstrated much higher catalytic efficiency than the CZ (CTAB-500) sample despite having a two times less SBET due to the promoting action of Ca and K inherited from sawdust and improved concentration of superoxide surface centers. Both facilitation of CO adsorption on peroxide and superoxide centers and increased oxygen mobility provide improvement in the high-temperature efficiency of biomorphic CZ in CO oxidation. The XRD, XPS and TPR data testify that Cu in modified systems partially exists as a separate CuO phase, in small amounts as Cu+, and partially is incorporated in the surface CuyCexZr1-x-yO2-z and/or CuyCe1-yO2-x phases. Modification with Cu enhances the low-temperature efficiency of CZ systems, prepared using both templates and calcined at 500 [degree]C. Cu-CZ (SD-500) was a bit less active than Cu-CZ (CTAB-500) only at 100-150 [degree]C, primarily due to the decreased CuO content, and the difference in CuO interaction with CZ support, found by TPR. Presumably CuO provides low-temperature CO oxidation through the Langmuir-Hinshelwood mechanism; the Cu+/Cu2+ pair can also participate as an additional redox pair in high-temperature CO oxidation by the Mars-van-Krevelen mechanism.