Dynamic investigation of electron trapping and charge decay in electron-irradiated Al2O3 in a scanning electron microscope: Methodology and mechanismsстатья
Статья опубликована в высокорейтинговом журнале
Статья опубликована в журнале из списка Web of Science и/или Scopus
Аннотация:The charging and discharging of polycristalline Al2O3 submitted to electron-irradiation in a scanning electron microscope (SEM) are investigated by means of the displacement current method. To circumvent experimental shortcomings inherent to the use of the basic sample holder, a redesign of the latter is proposed and tests are carried out to verify its operation. The effects of the primary beam accelerating voltage on charging, flashover and discharging phenomena during and after electron-irradiation are studied. The experimental results are then analyzed. In particular, the divergence between the experimental data and those predicted by the total electron emission yield approach (TEEYA) is discussed. A partial discharge was observed immediately after the end of the electron-irradiation exposure. The experimental data suggests, that the discharge is due to the evacuation to the ground, along the insulator surface, of released electrons from shallow traps at (or in the close vicinity of) the insulator/vacuum interface.