A phenomenological method of calculating the residual stresses and plastic deformations in a hollow surface-hardened cylindrical sampleстатьяПеревод
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 28 мая 2015 г.
Аннотация:A phenomenological method is proposed for calculating the residual stress and plastic deformation fields in a hollow surface-hardened cylindrical sample. Versions of the hardening are considered that lead to isotropy and anisotropy in the plastic deformations in the surface layer. A hardening anisotropy parameter is introduced that relates the axial and circumferential components of the residual plastic deformation tensor. The experimentally determined axial and/or circumferential components of the residual plastic stress tensor are used as the initial information. The tensor fields of the residual stresses and deformations are constructed assuming the hypothesis of surface hardening anisotropy and the absence of secondary plastic compression deformations and that the tangential components of the residual stress tensor and the plastic incompressibility of the material are small. A technique is developed for identifying the parameters of the proposed method. The adequacy is checked using experimental data for test pieces of type 45 and 12X18H10T steels hardened by hydro-shot blasting treatment and of type 45 steel hardened by treatment with a roller. Good agreement is observed between the calculated and experimental results. It is noted that the anisotropic hardening procedure leads to a substantial difference between the circumferential and axial components of the residual stresses in the hardened layer, unlike the case of isotropic hardening where they are practically identical.