Easily removed ceramic rods for casting gas-turbine engine blades using molding patternsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 26 марта 2018 г.
Аннотация:Methods have been developed for weakening and removing ceramic rods from a metal casting by means of polymorphic transformations in cristobalite and β-Ca2SiO4 during vibration in water containing surfactants without the use of aggressive and environmentally harmful reagents. The hot-bending strength (at 1050°C) of ceramic made from cristobalite was about 20 MPa while that of β-Ca2SiO4 at 1300°C was 18 – 24 MPa, which is adequate for use as a rod material. The use of carbamide formaldehyde resin with silicate sol as a binder for powders made from tridimite, mullite and zircon made it possible to weaken the rods, on cooling, as a result of polymorphism of cristobalite. The weakening and removal of the rods during vibration in water containing a surfactant was achieved with a polymorphic transformation from β-Ca2SiO4 into -Ca2SiO4 in mixes made from MgO, -Аl2O3, fused SiO2 and stabilized ZrO2.